Manmade Pyrolitic Graphite Sheets

Manmade Pyrolitic Graphite Sheets -700 to 1300W thermal conductivity -0.05 to 0.15mm available -1 side PET & 1 side adhesive

LGS800  high-performance  Manmade Pyrolitic Graphite Sheet is a thermal interface material which is very thin, synthetically

made, and has high thermal conductivity, and is made from a higly  oriented graphite polymer film. It is ideal for providing

thermal management/heat-sinking  in limited spaces or to provide supplemental heat-sinking in addition to conventional 

means.This material is flexible and can be cut into customizable shapes. 

Key properties:

1.Excellent thermal conductivity:700 to 1300 W/m.k 

   (2 to 4 times as high as copper,3 to 6 time as high as aluminum) 

2.Light weight: Specific gravity:0.85 to 2.17 g/cm3

   (1/4 to 1/10 of copper,1/1.3 to 1/3 of aluminum in density)

3.Flexible and easy to be cut or trimmed(withstands repeated bending)

Applications:

Cellular phone, DVC, PC and peripherals, pickup ,Semiconductor manufacturing equipment, MID table PC,

Game Console, Optical communications equipment

Physical properties:

Parameter			LGS800	LGS800	LGS800
Thickness			0.15±0.03 mm	0.07±0.015 mm	0.05±0.010 mm
Specific gravity			0.85 g/cm3	1.21 g/cm3	1.90 g/cm3
Thermal conductivity		a-b plane	700 W/(m-K)	1000 W/(m-K)	1300 W/(m-K)
Electrical conductivity			10000 S/cm	10000 S/cm	20000 S/cm
Extensional strength			19.6 MPa	22.0 MPa	30.0 MPa
Expansion Factor	a-b plane		9.3 10-7 1/K	9.3 10-7 1/K	9.3 10-7 1/K
	c axis		3.2 10-5 1/K	3.2 10-5 1/K	3.2 10-5 1/K
Thermal resistance			400°C
Bending test  (Times)  (R5/180°)			10000

Configurations available: customized sheet form, roll form.

Manmade Pyrolitic Graphite Sheets